China Wholesale China Direct Roving for Filament Winding
We now have one of the most advanced production machines, experienced and qualified engineers and workers, regarded quality manage systems and a friendly skilled sales group pre/after-sales support for China Wholesale China Direct Roving for Filament Winding, To provide customers with excellent equipment and services, and constantly develop new machine is our company’s business objectives. We look forward to your cooperation.
We now have one of the most advanced production machines, experienced and qualified engineers and workers, regarded quality manage systems and a friendly skilled sales group pre/after-sales support for China Direct Roving for Filament Winding, fiberglass roving, Regarding quality as survival, prestige as guarantee, innovation as motive force, development along with advanced technology, our group hopes to make progress together with you and make untiring efforts for the bright future of this industry.
PROPERTY
• Good process performance and low fuzz.
• Compatibility with a multiple of resin systems.
• Complete and fast wet-out.
• Good mechanical properties.
• Excellent acid corrosion resistance.
• Excellent aging resistance.
TECHNICAL PARAMETERS
| Linear Density (%) | Moisture Content (%) | Size Content (%) | Breakage Strength (N/Tex ) |
| ISO 1889 | ISO 3344 | ISO 1887 | ISO 3375 |
| ± 5 | ≤ 0.10 | 0.50 ± 0.15 | ≥0.40（≤17um）≥0.35（17～24um）≥0.30（≥24um） |
APPLICATION
Wide range of applications – suitable for a variety of scenarios, FRP tanks, FRP cooling towers, FRP model props, lighting tile sheds, boats, auto accessories, environmental protection projects, new roofing building materials, bathtubs, etc.
STORAGE
• Fiberglass products should be stored in a dry, cool, moisture-proof place.
• Fiberglass products should be kept in their original packaging before use. The room temperature and humidity should be kept at -10 °C ~ 35 °C and ≤ 80%, respectively.
• To ensure safety and avoid damaging the product, the stack height of the pallets should not exceed three layers.
• When pallets are stacked into 2 or 3 layers, special attention should be paid to moving the top tray correctly and smoothly
IDENTIFICATION
|
Glass Type |
E6 | ||||||
|
Type of Size |
Silane | ||||||
|
Size Code |
386H | ||||||
|
Linear Density (tex) |
300 | 600 | 1200 | 2200 | 2400 | 4800 | 9600 |
|
Filament Diameter (μm) |
13 | 17 | 17 | 23 | 17/24 | 24 | 31 |
MECHANICAL PROPERTIES
| Mechanical Properties |
Unit |
Value |
Resin |
Method |
| Tensile Strength |
MPa |
2765 |
UP |
ASTM D2343 |
| Tensile Modulus |
MPa |
81759 |
UP |
ASTM D2343 |
| Shear strength |
MPa |
2682 |
EP |
ASTM D2343 |
| Tensile Modulus |
MPa |
81473 |
EP |
ASTM D2343 |
| Shear strength |
MPa |
70 |
EP |
ASTM D2344 |
| Shear strength retention (72 hr boiling) |
% |
94 |
EP |
/ |
Memo:The above data are actual experimental values for E6DR24-2400-386H tand for reference only
PACKING
| Package height mm (in) | 260 (10.2) | 260 (10.2) |
| Package inside diameter mm (in) | 160 (6.3) | 160 (6.3) |
| Package outside diameter mm (in) | 275 (10.6) | 310 (12.2) |
| Package weight kg (lb) | 15.6 (34.4) | 22 (48.5) |
| Number of layers | 3 | 4 | 3 | 4 |
| Number of doffs per layer | 16 | 12 | ||
| Number of doffs per pallet | 48 | 64 | 36 | 48 |
| Net weight per pallet kg (lb) | 750 (1653.5) | 1000 (2204.6) | 792 (1746.1) | 1056 (2328.1) |
| Pallet length mm (in) | 1120 (44.1) | 1270 (50.0) | ||
| Pallet width mm (in) | 1120 (44.1) | 960 (37.8) | ||
| Pallet height mm (in) | 940 (37.0) | 1200 (47.2) | 940 (37.0) | 1200 (47.2) |
STORAGE
• Unless otherwise specified, the fiberglass products should be stored in a dry,cool and moisture-proof area.
• The fiberglass products should remain in their original package until prior to use. The room temperature and humidity should be always maintained at -10℃~35℃ and ≤80% respectively.
• To ensure safety and avoid damage to the product, the pallets should not be stacked more than three layers high.
• When the pallets are stacked in 2 or 3 layers, special care should be taken to correctly and smoothly move the top palleWe now have one of the most advanced production machines, experienced and qualified engineers and workers, regarded quality manage systems and a friendly skilled sales group pre/after-sales support for China Wholesale China Direct Roving for Filament Winding, To provide customers with excellent equipment and services, and constantly develop new machine is our company’s business objectives. We look forward to your cooperation.
China Wholesale China Direct Roving for Filament Winding, Fiberglass Roving, Regarding quality as survival, prestige as guarantee, innovation as motive force, development along with advanced technology, our group hopes to make progress together with you and make untiring efforts for the bright future of this industry.