E-Glass Fiberglass Direct and Assembled Roving

short description:

Fiberglass Direct Roving is coated with a silane-based sizing compatible with unsaturated polyester, vinyl ester, and epoxy resins. It is designed for filament winding,pultrusion, and weaving applications.

MOQ:10 tons

Send email to us

Product Detail

Product Tags

We are also focusing on improving the stuff management and QC system so that we could keep great advantage in the fiercely-competitive business for E-Glass Fiberglass Direct and Assembled Roving, We have been wanting ahead to setting up cooperative associations along with you. Make sure you contact us for more data.
We are also focusing on improving the stuff management and QC system so that we could keep great advantage in the fiercely-competitive business for China Assembled Roving and Direct Roving, The president and all the company members would like to provide professional products and services for customers and sincerely welcome and cooperate with all native and foreign customers for a bright future.

PROPERTY

• Good process performance and low fuzz.
• Compatibility with multiple resin systems.
• Complete and fast wet-out.
• Good mechanical properties.
• Excellent acid corrosion resistance.
• Excellent aging resistance.

We have many types of fiberglass roving: panel roving, spray up roving, SMC roving, direct roving,c glass roving, and fiberglass roving for chopping.

TECHNICAL PARAMETERS

Linear Density (%)	Moisture Content (%)	Size Content (%)	Breakage Strength (N/Tex )
ISO 1889	ISO 3344	ISO 1887	ISO 3375
± 5	≤ 0.10	0.50 ± 0.15	≥0.40（≤17um）≥0.35（17～24um）≥0.30（≥24um）

APPLICATION

Wide range of applications – suitable for a variety of scenarios, FRP tanks, FRP cooling towers, FRP model props, lighting tile sheds, boats, auto accessories, environmental protection projects, new roofing building materials, bathtubs, etc.

Our fiberglass mats are of several types: fiberglass surface mats, fiberglass chopped strand mats, and continuous fiberglass mats. The chopped strand mat is divided into emulsion and powder glass fiber mats.

STORAGE

• Fiberglass products should be stored in a dry, cool, moisture-proof place.
• Fiberglass products should be kept in their original packaging before use. The room temperature and humidity should be kept at -10 °C ~ 35 °C and ≤ 80%, respectively.
• To ensure safety and avoid damaging the product, the stack height of the pallets should not exceed three layers.
• When pallets are stacked into 2 or 3 layers, special attention should be paid to moving the top tray correctly and smoothly

IDENTIFICATION

Glass Type	E6
Type of Size	Silane
Size Code	386H
Linear Density (tex)	300	600	1200	2200	2400	4800	9600
Filament Diameter (μm)	13	17	17	23	17/24	24	31

MECHANICAL PROPERTIES

Mechanical Properties	Unit	Value	Resin	Method
Tensile Strength	MPa	2765	UP	ASTM D2343
Tensile Modulus	MPa	81759	UP	ASTM D2343
Shear strength	MPa	2682	EP	ASTM D2343
Tensile Modulus	MPa	81473	EP	ASTM D2343
Shear strength	MPa	70	EP	ASTM D2344
Shear strength retention (72 hr boiling)	%	94	EP	/

Memo: The above data are actual experimental values for E6DR24-2400-386H and for reference only

PACKING

Package height mm (in)	260 (10.2)	260 (10.2)
Package inside diameter mm (in)	160 (6.3)	160 (6.3)
Package outside diameter mm (in)	275 (10.6)	310 (12.2)
Package weight kg (lb)	15.6 (34.4)	22 (48.5)

Number of layers	3	4	3	4
Number of doffs per layer	16		12
Number of doffs per pallet	48	64	36	48
Net weight per pallet kg (lb)	750 (1653.5)	1000 (2204.6)	792 (1746.1)	1056 (2328.1)

Pallet length mm (in)	1120 (44.1)		1270 (50.0)
Pallet width mm (in)	1120 (44.1)		960 (37.8)
Pallet height mm (in)	940 (37.0)	1200 (47.2)	940 (37.0)	1200 (47.2)

STORAGE

• Unless otherwise specified, the fiberglass products should be stored in a dry,cool and moisture-proof area.

• The fiberglass products should remain in their original package until prior to use. The room temperature and humidity should be always maintained at -10℃~35℃ and ≤80% respectively.

• To ensure safety and avoid damage to the product, the pallets should not be stacked more than three layers high.

• When the pallets are stacked in 2 or 3 layers, special care should be taken to correctly and smoothly move the top palleWe are also focusing on improving the staff management and QC system so that we could keep a great advantage in the fiercely-competitive business for Special Design for E-Glass Fiberglass Direct and Assembled Roving, We have been wanting ahead to setting up cooperative associations along with you. Make sure you contact us for more data.
Special Design for China Assembled Roving and Direct Roving, The president and all the company members would like to provide professional products and services for customers and sincerely welcome and cooperate with all native and foreign customers for a bright future.

Previous: Fiberglass Roofing Tissue/ Surface Tissue Glass Fiber Surface Mat

Next: 2400tex Assembled Fiberglass Panel Roving OEM China Good Translucent

China Assembled Roving and Direct Roving