Low MOQ for Ecr Fiberglass Cloth - Fiberglass Direct Roving E-glass General Purpose – Dujiang
We believe that long term partnership is a result of high quality, value added service, rich experience and personal contact for High Silica Fiberglass, unsaturated polyester resin manufacturers, Sticky Fiber Glass Mesh, To supply prospects with superb equipment and providers, and constantly build new machine is our company's organization objectives. We look ahead for your cooperation.
Low MOQ for Ecr Fiberglass Cloth - Fiberglass Direct Roving E-glass General Purpose – Dujiang Detail:
PROPERTY
• Good process performance and low fuzz.
• Compatibility with multiple resin systems.
• Complete and fast wet-out.
• Good mechanical properties.
• Excellent acid corrosion resistance.
• Excellent aging resistance.
We have many types of fiberglass roving: panel roving, spray up roving, SMC roving, direct roving,c glass roving, and fiberglass roving for chopping.
TECHNICAL PARAMETERS
| Linear Density (%) | Moisture Content (%) | Size Content (%) | Breakage Strength (N/Tex ) |
| ISO 1889 | ISO 3344 | ISO 1887 | ISO 3375 |
| ± 5 | ≤ 0.10 | 0.50 ± 0.15 | ≥0.40（≤17um）≥0.35（17～24um）≥0.30（≥24um） |
APPLICATION
Wide range of applications – suitable for a variety of scenarios, FRP tanks, FRP cooling towers, FRP model props, lighting tile sheds, boats, auto accessories, environmental protection projects, new roofing building materials, bathtubs, etc.
Our fiberglass mats are of several types: fiberglass surface mats, fiberglass chopped strand mats, and continuous fiberglass mats. The chopped strand mat is divided into emulsion and powder glass fiber mats.
STORAGE
• Fiberglass products should be stored in a dry, cool, moisture-proof place.
• Fiberglass products should be kept in their original packaging before use. The room temperature and humidity should be kept at -10 °C ~ 35 °C and ≤ 80%, respectively.
• To ensure safety and avoid damaging the product, the stack height of the pallets should not exceed three layers.
• When pallets are stacked into 2 or 3 layers, special attention should be paid to moving the top tray correctly and smoothly
IDENTIFICATION
|
Glass Type |
E6 | ||||||
|
Type of Size |
Silane | ||||||
|
Size Code |
386H | ||||||
|
Linear Density (tex) |
300 | 600 | 1200 | 2200 | 2400 | 4800 | 9600 |
|
Filament Diameter (μm) |
13 | 17 | 17 | 23 | 17/24 | 24 | 31 |
MECHANICAL PROPERTIES
| Mechanical Properties |
Unit |
Value |
Resin |
Method |
| Tensile Strength |
MPa |
2765 |
UP |
ASTM D2343 |
| Tensile Modulus |
MPa |
81759 |
UP |
ASTM D2343 |
| Shear strength |
MPa |
2682 |
EP |
ASTM D2343 |
| Tensile Modulus |
MPa |
81473 |
EP |
ASTM D2343 |
| Shear strength |
MPa |
70 |
EP |
ASTM D2344 |
| Shear strength retention (72 hr boiling) |
% |
94 |
EP |
/ |
Memo: The above data are actual experimental values for E6DR24-2400-386H and for reference only
PACKING
| Package height mm (in) | 260 (10.2) | 260 (10.2) |
| Package inside diameter mm (in) | 160 (6.3) | 160 (6.3) |
| Package outside diameter mm (in) | 275 (10.6) | 310 (12.2) |
| Package weight kg (lb) | 15.6 (34.4) | 22 (48.5) |
| Number of layers | 3 | 4 | 3 | 4 |
| Number of doffs per layer | 16 | 12 | ||
| Number of doffs per pallet | 48 | 64 | 36 | 48 |
| Net weight per pallet kg (lb) | 750 (1653.5) | 1000 (2204.6) | 792 (1746.1) | 1056 (2328.1) |
| Pallet length mm (in) | 1120 (44.1) | 1270 (50.0) | ||
| Pallet width mm (in) | 1120 (44.1) | 960 (37.8) | ||
| Pallet height mm (in) | 940 (37.0) | 1200 (47.2) | 940 (37.0) | 1200 (47.2) |
STORAGE
• Unless otherwise specified, the fiberglass products should be stored in a dry,cool and moisture-proof area.
• The fiberglass products should remain in their original package until prior to use. The room temperature and humidity should be always maintained at -10℃~35℃ and ≤80% respectively.
• To ensure safety and avoid damage to the product, the pallets should not be stacked more than three layers high.
• When the pallets are stacked in 2 or 3 layers, special care should be taken to correctly and smoothly move the top palle
Product detail pictures:
Related Product Guide:
Good quality comes 1st; assistance is foremost; business enterprise is cooperation" is our business enterprise philosophy which is regularly observed and pursued by our company for Low MOQ for Ecr Fiberglass Cloth - Fiberglass Direct Roving E-glass General Purpose – Dujiang , The product will supply to all over the world, such as: Oman, Munich, Colombia, You can let us know your idea to develop unique design for your own model to prevent too much similar parts in the market! We will provide our best service to satisfy all your needs! You should contact us right away!
By Annabelle from Belarus - 2017.04.08 14:55
The customer service staff is very patient and has a positive and progressive attitude to our interest, so that we can have a comprehensive understanding of the product and finally we reached an agreement, thanks!
By Laurel from Riyadh - 2017.01.28 18:53