• Good process performance and low fuzz.
• Compatibility with multiple resin systems.
• Complete and fast wet-out.
• Good mechanical properties.
• Excellent acid corrosion resistance.
• Excellent aging resistance.
We have many types of fiberglass roving: panel roving, spray up roving, SMC roving, direct roving,c glass roving, and fiberglass roving for chopping.
Linear Density (%) | Moisture Content (%) | Size Content (%) | Breakage Strength (N/Tex ) |
ISO 1889 | ISO 3344 | ISO 1887 | ISO 3375 |
± 5 | ≤ 0.10 | 0.50 ± 0.15 | ≥0.40(≤17um)≥0.35(17~24um)≥0.30(≥24um) |
Wide range of applications – suitable for a variety of scenarios, FRP tanks, FRP cooling towers, FRP model props, lighting tile sheds, boats, auto accessories, environmental protection projects, new roofing building materials, bathtubs, etc.
Our fiberglass mats are of several types: fiberglass surface mats, fiberglass chopped strand mats, and continuous fiberglass mats. The chopped strand mat is divided into emulsion and powder glass fiber mats.
• Fiberglass products should be stored in a dry, cool, moisture-proof place.
• Fiberglass products should be kept in their original packaging before use. The room temperature and humidity should be kept at -10 °C ~ 35 °C and ≤ 80%, respectively.
• To ensure safety and avoid damaging the product, the stack height of the pallets should not exceed three layers.
• When pallets are stacked into 2 or 3 layers, special attention should be paid to moving the top tray correctly and smoothly
Glass Type |
E6 | ||||||
Type of Size |
Silane | ||||||
Size Code |
386H | ||||||
Linear Density (tex) |
300 | 600 | 1200 | 2200 | 2400 | 4800 | 9600 |
Filament Diameter (μm) |
13 | 17 | 17 | 23 | 17/24 | 24 | 31 |
Mechanical Properties |
Unit |
Value |
Resin |
Method |
Tensile Strength |
MPa |
2765 |
UP |
ASTM D2343 |
Tensile Modulus |
MPa |
81759 |
UP |
ASTM D2343 |
Shear strength |
MPa |
2682 |
EP |
ASTM D2343 |
Tensile Modulus |
MPa |
81473 |
EP |
ASTM D2343 |
Shear strength |
MPa |
70 |
EP |
ASTM D2344 |
Shear strength retention (72 hr boiling) |
% |
94 |
EP |
/ |
Memo: The above data are actual experimental values for E6DR24-2400-386H and for reference only
Package height mm (in) | 260 (10.2) | 260 (10.2) |
Package inside diameter mm (in) | 160 (6.3) | 160 (6.3) |
Package outside diameter mm (in) | 275 (10.6) | 310 (12.2) |
Package weight kg (lb) | 15.6 (34.4) | 22 (48.5) |
Number of layers | 3 | 4 | 3 | 4 |
Number of doffs per layer | 16 | 12 | ||
Number of doffs per pallet | 48 | 64 | 36 | 48 |
Net weight per pallet kg (lb) | 750 (1653.5) | 1000 (2204.6) | 792 (1746.1) | 1056 (2328.1) |
Pallet length mm (in) | 1120 (44.1) | 1270 (50.0) | ||
Pallet width mm (in) | 1120 (44.1) | 960 (37.8) | ||
Pallet height mm (in) | 940 (37.0) | 1200 (47.2) | 940 (37.0) | 1200 (47.2) |
• Unless otherwise specified, the fiberglass products should be stored in a dry,cool and moisture-proof area.
• The fiberglass products should remain in their original package until prior to use. The room temperature and humidity should be always maintained at -10℃~35℃ and ≤80% respectively.
• To ensure safety and avoid damage to the product, the pallets should not be stacked more than three layers high.
• When the pallets are stacked in 2 or 3 layers, special care should be taken to correctly and smoothly move the top palle
For inquiries about our products or pricelist, please leave your email to us and we will be in touch within 24 hours.