Manufacturer of 200tex Fiberglass Direct Roving for Mesh
we can easily provide top quality solutions, competitive value and best client company. Our destination is “You come here with difficulty and we provide you a smile to take away” for Manufacturer of 200tex Fiberglass Direct Roving for Mesh, We promise to try our best to offer you with top quality and effective products and services.
we can easily provide top quality solutions, competitive value and best client company. Our destination is “You come here with difficulty and we provide you a smile to take away” for 200tex Direct Roving, China Fiberglass Roving, Our company always committed to meet your quality demand, price points and sales target. Warmly welcome you open the boundaries of communication. It is our great pleasure to service you if you require a trusted supplier and value information.
PROPERTY
• Good process performance and low fuzz.
• Compatibility with multiple resin systems.
• Complete and fast wet-out.
• Good mechanical properties.
• Excellent acid corrosion resistance.
• Excellent aging resistance.
We have many types of fiberglass roving: panel roving, spray up roving, SMC roving, direct roving,c glass roving, and fiberglass roving for chopping.
TECHNICAL PARAMETERS
| Linear Density (%) | Moisture Content (%) | Size Content (%) | Breakage Strength (N/Tex ) |
| ISO 1889 | ISO 3344 | ISO 1887 | ISO 3375 |
| ± 5 | ≤ 0.10 | 0.50 ± 0.15 | ≥0.40（≤17um）≥0.35（17～24um）≥0.30（≥24um） |
APPLICATION
Wide range of applications – suitable for a variety of scenarios, FRP tanks, FRP cooling towers, FRP model props, lighting tile sheds, boats, auto accessories, environmental protection projects, new roofing building materials, bathtubs, etc.
Our fiberglass mats are of several types: fiberglass surface mats, fiberglass chopped strand mats, and continuous fiberglass mats. The chopped strand mat is divided into emulsion and powder glass fiber mats.
STORAGE
• Fiberglass products should be stored in a dry, cool, moisture-proof place.
• Fiberglass products should be kept in their original packaging before use. The room temperature and humidity should be kept at -10 °C ~ 35 °C and ≤ 80%, respectively.
• To ensure safety and avoid damaging the product, the stack height of the pallets should not exceed three layers.
• When pallets are stacked into 2 or 3 layers, special attention should be paid to moving the top tray correctly and smoothly
IDENTIFICATION
|
Glass Type |
E6 | ||||||
|
Type of Size |
Silane | ||||||
|
Size Code |
386H | ||||||
|
Linear Density (tex) |
300 | 600 | 1200 | 2200 | 2400 | 4800 | 9600 |
|
Filament Diameter (μm) |
13 | 17 | 17 | 23 | 17/24 | 24 | 31 |
MECHANICAL PROPERTIES
| Mechanical Properties |
Unit |
Value |
Resin |
Method |
| Tensile Strength |
MPa |
2765 |
UP |
ASTM D2343 |
| Tensile Modulus |
MPa |
81759 |
UP |
ASTM D2343 |
| Shear strength |
MPa |
2682 |
EP |
ASTM D2343 |
| Tensile Modulus |
MPa |
81473 |
EP |
ASTM D2343 |
| Shear strength |
MPa |
70 |
EP |
ASTM D2344 |
| Shear strength retention (72 hr boiling) |
% |
94 |
EP |
/ |
Memo: The above data are actual experimental values for E6DR24-2400-386H and for reference only
PACKING
| Package height mm (in) | 260 (10.2) | 260 (10.2) |
| Package inside diameter mm (in) | 160 (6.3) | 160 (6.3) |
| Package outside diameter mm (in) | 275 (10.6) | 310 (12.2) |
| Package weight kg (lb) | 15.6 (34.4) | 22 (48.5) |
| Number of layers | 3 | 4 | 3 | 4 |
| Number of doffs per layer | 16 | 12 | ||
| Number of doffs per pallet | 48 | 64 | 36 | 48 |
| Net weight per pallet kg (lb) | 750 (1653.5) | 1000 (2204.6) | 792 (1746.1) | 1056 (2328.1) |
| Pallet length mm (in) | 1120 (44.1) | 1270 (50.0) | ||
| Pallet width mm (in) | 1120 (44.1) | 960 (37.8) | ||
| Pallet height mm (in) | 940 (37.0) | 1200 (47.2) | 940 (37.0) | 1200 (47.2) |
STORAGE
• Unless otherwise specified, the fiberglass products should be stored in a dry,cool and moisture-proof area.
• The fiberglass products should remain in their original package until prior to use. The room temperature and humidity should be always maintained at -10℃~35℃ and ≤80% respectively.
• To ensure safety and avoid damage to the product, the pallets should not be stacked more than three layers high.
• When the pallets are stacked in 2 or 3 layers, special care should be taken to correctly and smoothly move the top palle
we can easily provide top-quality solutions, competitive value, and the best client company. Our destination is “You come here with difficulty and we provide you a solution to take away” for the Manufacturer of 200tex Fiberglass Direct Roving for Mesh, We promise to try our best to offer you top quality and effective products and services.
Manufacturer of China Fiberglass Roving and 200tex Direct Roving, Our company is always committed to meeting your quality demand, price points, and sales target. Warmly welcome you to open the boundaries of communication. It is our great pleasure to service you if you require a trusted supplier and valuable information.