Persisting in "High top quality, Prompt Delivery, Aggressive Price", now we have established long-term cooperation with customers from the two overseas and domestically and get new and aged clients' large comments for Assembled Winding Roving, Chopped Strand Mat Fiberglass, Carbon Fiber Cloth Fabric, We sincerely expect exchange and cooperation with you. Let us move forward hand in hand and achieve win-win situation.

Rapid Delivery for Fiber Glass Cloth - E-Glass Chopped Strand Mat Emulsion – Dujiang Detail:

Applications and Requirements

1.Hand lay-up: Hand lay-up is the main method of FRP production. Fiberglass chopped strand mats, continuous mats and stitched mats can all be used in hand lay-up. The use of stitch-bonded mat can reduce the number of layers and improve the efficiency of hand lay-up operations. However, because the stitchbonded mat contains more chemical fiber stitchbonding threads, the bubbles are not easy to drive away, and the fiberglass products have many needle-shaped bubbles, and the surface feels rough and not smooth. In addition, the stitched mat is a heavy fabric, and the mold coverage is shorter than that of the cut mat and the continuous mat. When making products with complex shapes, it is easy to form voids at the bend. The hand lay-up process requires the mat to have the characteristics of fast resin infiltration rate, easy elimination of air bubbles and good mold coverage.

2.Pultrusion: The pultrusion process is one of the main uses of continuous felt and stitched felt. Generally, it is used in combination with untwisted roving. Using continuous mat and stitched mat as pultruded products can significantly improve the hoop and transverse strength of the products and prevent the products from cracking. The pultrusion process requires the mat to have uniform fiber distribution, high tensile strength, fast resin infiltration rate, good flexibility and mold filling, and the mat should have a certain continuous length.

3.RTM: Resin transfer molding (RTM) is a closed mold molding process. It is composed of two half-moulds, a female mold and a male mold, a pressurizing pump and an injection gun, without a press. The RTM process typically uses continuous and stitch-bonded mats rather than chopped strand mats. The mat sheet is required to have the characteristics that the mat sheet should be easily saturated with resin, good air permeability, good resin scour resistance and good overmoldability.

4.Winding process: chopped strand mats and continuous mats are generally used for winding and forming resin-rich layers mainly used for products, including inner lining layers and outer surface layers. The requirements for the glass fiber mat in the winding process are basically similar to those in the hand lay-up method.

5.Centrifugal casting molding: chopped strand mat is usually used as raw material. The chopped strand mat is pre-laid in the mold, and then the resin is added into the rotating open mold cavity, and the air bubbles are discharged by centrifugation to make the product dense. The mat sheet is required to have the characteristics of easy penetration and good air permeability.

INSTRUCTION

E-Glass Chopped Strand Mat Emulsion
			Quality Index-1040
			225G	300G	450G
Test Item	Criterion According	Unit	Standard	Standard	Standard
GLASS TYPE	G/T 17470-2007	%	R₂O<0.8%	R₂O<0.8%	R₂O<0.8%
COUPLING AGENT	G/T 17470-2007	%	SILANE	SILANE	SILANE
Area Weight	GB/T 9914.3	g/m2	225±45	300±60	450±90
Loi Content	GB/T 9914.2	%	1.5-12	1.5-8.5	1.5-8.5
Tension Strength CD	GB/T 6006.2	N	≥40	≥40	≥40
Tension Strength MD	GB/T 6006.2	N	≥40	≥40	≥40
Water Content	GB/T 9914.1	%	≤0.5	≤0.5	≤0.5
Permeation Rate	G/T 17470	s	<250	<250	<250
Width	G/T 17470	mm	±5	±5	±5
Bending strength	G/T 17470	MPa	Standard ≧123	Standard ≧123	Standard ≧123
Bending strength	G/T 17470	MPa	Wet ≧103	Wet ≧103	Wet ≧103
Test Condition
Ambent Temperature（℃）		10	Ambient Humidity(%)

INSTRUCTION

Product detail pictures:

Related Product Guide:

To be the stage of realizing dreams of our employees! To build a happier, far more united and far more specialist team! To reach a mutual profit of our customers, suppliers, the society and ourselves for Rapid Delivery for Fiber Glass Cloth - E-Glass Chopped Strand Mat Emulsion – Dujiang , The product will supply to all over the world, such as: Luxemburg, Swiss, Auckland, Many years of work experience, we have realized the importance of providing good quality products and the best before-sales and after-sales services. Most problems between suppliers and clients are due to poor communication. Culturally, suppliers can be reluctant to question things they do not understand. We break down those barriers to ensure you get what you want to the level you expect, when you want it. faster delivery time and the product you want is our Criterion .

160gsm Twill Fiberglass Fabrics